hot deformation and processing map of a typical al–zn–mg–cu alloy，成果详细信息-凯发网

the effects of the deformation temperature and strain rate on the high-temperature flow behavior of 7075 aluminum alloy were studied by hot compressive tests. based on the experimental data, the efficiencies of power dissipation and instability parameter were evaluated, and processing maps were constructed by superimposing the instability map over the power dissipation map. microstructural evolution of 7075 aluminum alloy during the hot compression was analyzed to correlate with the processing maps. results show that (1) the flow stresses increase with the increase of strain rate and the decrease of deformation temperature; (2) the high-angle boundaries and coarse precipitations distributing in the grain interior/boundaries, which may result in the deep inter-granular corrosion and large areas of denudation layer, should be avoided in the microstructures of the final products; (3) the optimum hot working domain is the temperature range of 623-723 k and strain rate range of 0.001-0.05 s-1.