microstructural evolution of a nickel-based superalloy during hot deformation

, , , , , , ,

materials & design, 2015, 77: 41–49.,-0001,():

url:

摘要/描述

hot compressive tests of a nickel-based superalloy are performed under the strain rate range of 0.001–1 s−1 and deformation temperature range of 920–1040 °c. optical microscopy (om) and transmission electron microscopy (tem) are employed to investigate the evolution of dynamic recrystallized (drx) grain and dislocation substructure. it is found that the effects of deformation degree, strain rate and deformation temperature on drx grain are significant. when the deformation degree or temperature is increased, the number of drx grains rapidly increases. but, the increase of strain rate reduces the number of drx grains. the dislocation substructure is also very sensitive to the deformation degree, strain rate and deformation temperature. with the increase of deformation degree, the evolution of dislocation substructure can be characterized as: high dislocation density → dislocation network → subgrain → drx grain. under high deformation temperatures or low strain rates, the dislocation substructure can be easily annihilated and rearranged because of the occurrence of drx. based on the evaluated drx volume fractions, the contour map is constructed to optimize the hot deformation parameters.

关键词:
  • 问答

    暂无问题,成为第一个提问者

【免责声明】以下全部内容由[蔺永诚]上传于[2015年04月19日 10时17分32秒],凯发k8国际首页的版权归原创者所有。本文仅代表作者本人观点,与本网站无关。本网站对文中陈述、观点判断保持中立,不对所包含内容的准确性、可靠性或完整性提供任何明示或暗示的保证。请读者仅作参考,并请自行承担全部责任。

我要评论

全部评论 0

本学者其他成果

同领域成果

网站地图